TCKT120 96% HAP alumina ceramic parts for charging relay
1. Description:
TCKT120 96% HAP alumina ceramic parts for charging relay is made of alumina materials, and it is thick-film nickel plating on surface connection header.It is suitable for brazing different materials such as copper and alloys. It can meet the requirements of at the same time, and it can . Reaching the , it is currently an excellent technical solution in the field of
2. Key Words:
Seismic and tensile,withstand high current and arc shock,reliable sealing and insulation standards of DC high-voltage relays,new energy vehicles and DC high-voltage electronic control,manufacture samples , open mould ,aluminum oxide,thick-film nickel plating technology,copper and alloys,great limberness,Good corrosion resistance,High intensity,Good high-temperature resistance performance,High purity.
3. Technical Parameters table:
| Product Parameters |
| Physical Property | Material | 95% Alumina |
| Production Process | Dry Pressing |
| Product Dimension | Per customers' drawing |
| Density (g/cm3) | 3.70-3.75g/cm3 |
| Water Absorption | 0% |
| Mechanical Performance | Flexural Strength (Mpa) | 310Mpa |
| Modulus of Elasticity (Gpa) | 310Gpa |
| Hardness (Gpa) | 12.9Gpa |
| Poisson Ratio | 0.23 |
| Thermal Character | Linear Thermal Expansion Coefficient | 7.2 |
| Heat Conductivity (W/mk) | 23 |
| Electrical Property | Dielectric Constant | 9.2 |
| Dielectric Loss Tangent (x10-4) | 8 |
| Insulation Strength (x106V/M) | 15 |
| Metalized Ceramic Performance | Air Tightness (Pa·m3/s) | ≤10-8 |
| Bulk Resistivity (Ω·cm) | ≥1010 (20°C), ≥106 (300°C) |
| Bonding Strength (Mpa) | ≥120Mpa |
| Metallization Thickness (μm) | ≥20μm |
Product Tags:
|
|
Hardness 12.9Gpa 96% HAP Alumina Ceramic Parts For Charging Relay Images
|